Industry Specifications:
- ASTM B32: Sn50
- J Industry: Sn50A
Nominal Composition:
Tin 50.00, Lead 50.00
Liquidus:
421 °F
Liquidus:
216 °C
Solidus:
361 °F
Solidus:
183 °C
Industry Specifications:
- ASTM B32: Sb5
- J Industry: Sb05A
Nominal Composition:
Tin 95.00, Antimony 5.00
Liquidus:
464 °F
Liquidus:
240 °C
Solidus:
450 °F
Solidus:
232 °C
Industry Specifications:
- AMS: 4769
- ISO 17672: Ag 345
- Federal QQ-B-654: GR VII
- AWS: BAg-1
Nominal Composition:
Silver 45.00, Copper 15.00, Zinc 16.00, Cadmium 24.00
Liquidus:
1145 °F
Liquidus:
618 °C
Solidus:
1125 °F
Solidus:
607 °C
Industry Specifications:
- ISO 17672: CuP 181
- AWS: BCuP-2
Nominal Composition:
Copper 92.75, Phosphorous 7.25
Liquidus:
1460 °F
Liquidus:
793 °C
Solidus:
1310 °F
Solidus:
710 °C
Nominal Composition:
Aluminum 22.00, Zinc 78.00
Liquidus:
900 °F
Liquidus:
482 °C
Solidus:
800 °F
Solidus:
427 °C
Industry Specifications:
- AMS: 4788
- ISO 17672: Ag 450
- AWS: BAg-24
Nominal Composition:
Silver 50.00, Copper 20.00, Zinc 28.00, Nickel 2.00
Liquidus:
1305 °F
Liquidus:
707 °C
Solidus:
1220 °F
Solidus:
660 °C
Nominal Composition:
Silver 6.00, Copper 88.00, Phosphorous 6.00
Liquidus:
1300 °F
Liquidus:
704 °C
Solidus:
1190 °F
Solidus:
643 °C
Industry Specifications:
- ISO 17672: CuP 284
- Federal QQ-B-654: BCuP-5
- AWS: BCuP-5
Nominal Composition:
Silver 15.00, Copper 80.00, Phosphorous 5.00
Liquidus:
1300 °F
Liquidus:
704 °C
Solidus:
1190 °F
Solidus:
643 °C
Industry Specifications:
- ISO 17672: CuP 280
- AWS: BCuP-6
Nominal Composition:
Silver 2.00, Copper 91.00, Phosphorous 7.00
Liquidus:
1325 °F
Liquidus:
718 °C
Solidus:
1190 °F
Solidus:
643 °C
Industry Specifications:
- ISO 17672: CuP 281
- AWS: BCuP-3
Nominal Composition:
Silver 5.00, Copper 89.00, Phosphorous 6.00
Liquidus:
1325 °F
Liquidus:
718 °C
Solidus:
1190 °F
Solidus:
643 °C
Industry Specifications:
- ASTM B32: Sn96
- J Industry: Sn96A
Nominal Composition:
Silver 3.60, Tin 96.40
Liquidus:
430 °F
Liquidus:
221 °C
Solidus:
430 °F
Solidus:
221 °C
Nominal Composition:
Silver 0.50, Tin 95.50, Copper 4.00
Liquidus:
660 °F
Liquidus:
349 °C
Solidus:
440 °F
Solidus:
227 °C
Nominal Composition:
Silver 5.60, Tin 94.40
Liquidus:
536 °F
Liquidus:
280 °C
Solidus:
430 °F
Solidus:
221 °C
Nominal Composition:
Copper 3.50, Tin 96.50
Liquidus:
572 °F
Liquidus:
300 °C
Solidus:
440 °F
Solidus:
227 °C
Industry Specifications:
- ASTM B32: Sn95
- J Industry: Sn95E
Nominal Composition:
Silver 4.60, Tin 95.40
Liquidus:
473 °F
Liquidus:
245 °C
Solidus:
430 °F
Solidus:
221 °C
Industry Specifications:
- ISO 17672: Ag 245
- Federal QQ-B-654: BAg-5
- AWS: BAg-5
Nominal Composition:
Silver 45.00, Copper 30.00, Zinc 25.00
Liquidus:
1370 °F
Liquidus:
743 °C
Solidus:
1225 °F
Solidus:
663 °C